Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa

Minimum Order Quantity : 1000KG Price : 700-1200
Packaging Details : 25kg/bag or 1000kg/bag Delivery Time : 1 week
Payment Terms : L/C, T/T, D/A, T/T Supply Ability : 500 MT per month
Place of Origin: China Brand Name: Anan
Certification: UL,Reach,RoHs,SGS Model Number: PVC Granules

Detail Information

Material: Plastic PVC Granules Color: Natural,Black,Green,Red,Color Customised
Tensile Strength: 12.5MPa Elongation: 150%
Shape: PVC Granules Operation: Extrusion Or Injection Process
Hardness: 86A-90A Sample: For Free
Volume Resistivity: 1*10~12 Temperature Resistance: -40, 105℃
High Light:

Reach PVC Cable Compound

,

12.5Mpa PVC Cable Compound

,

85A Hardness 85A PVC Compound

Product Description

Cable PVC Compounds Hardness 85A 1.5g/cm3 Cable Insulation Tensile Strength 12.5Mpa

 

Specs Features Application


Common Insulation

Component Wire Material

Passed UL test, Cold-form test -20 ℃,

Heat resistance

grade: 60℃ 75℃ 90℃ 105℃,

Combustion test: VW-1 FT2, Environment friendly.


Suites for various indoor insulation

component wire material.


Cold – Resistant Insulation

Component Wire Material


Passed UL test, Cold-form test -40 ℃, Heat resistance grade:

60℃ 75℃ 90℃ 105℃,

Combustion test: VW-1 FT2, Environment friendly.


Suits for outdoor -40℃ cold – resistant insulation component

wire material

 

1.Technical specifications of 70 ℃ pvc compound

 

Tensile strength MPa 20.5
Fracture tensile strain % 320
Ageing temperature 100
Ageing time h 168
Tensile strength after ageing MPa 22.5
Max change of tensile strength % +12
After ageing fracture tensile strain % 290
Max change of fracture tensile strain % -10
Thermal deformation % 28
Thermal ageing quality loss g/m2 19
200℃ thermal stability time min 90
20℃ volume resistivity Ω.cm 2.0*1011

 

Technical specifications of 90 ℃ pvc resin compound

 

Tensile strength MPa 20
Fracture tensile strain % 330
Ageing temperature 100
Ageing time h 240
Tensile strength after ageing MPa 21.5
Max change of tensile strength % +8
After ageing fracture tensile strain % 310
Max change of fracture tensile strain % -6
Thermal deformation % 28
Thermal ageing quality loss g/m2 9
200℃ thermal stability time min 120
20℃ volume resistivity Ω.cm 2.0*1010

 

2,Use and standard: wire and cable

 

3,Process: extrusion

 

4,Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.

 

5,color: Any colors, base on requirement.

 

6,Packing: 25kg net weight per in a kraft bag.

 

7, Transportation and storage:

This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.

 

We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.

 

 

 

Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa 0Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa 1

 

Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa 2Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa 3

Hardness 85A 1.5g/Cm3 PVC Cable Compound Insulation Tensile Strength 12.5Mpa 4

 

You Might Be Into These
Get in touch with us

Enter Your Message

fillertwine@longtai168.com
+8613580878248
zhangmeilan332
+86 13580878248